TDS HARTCRYL 4.1
Fast drying quality two component polyurethane autocryl.Developed for spot repair and undertaking block repairs. Good hardness, good weather resistance with good film appearance. |
||
Relic Clear (part A) : – Hardener (part B) : – | ||
Packing size : Part A : – ml Part B : – ml | ||
Mixing ratio * | Viscosity | Pot Life |
4 : 1 (by volume) |
13.6 sec DIN 4 (Part A + Part B) | 2-3 hours |
Hardness pendulum day 7 on pot | Spray Viscosity | Spray Nozzle |
76 (osc,konig) | 13 sec NK2 @ 25˚C | 1.3-1.4 |
Spray pressure | Number of Coat | Total film build |
2.0 – 3.0 BAR | 2 Coats | 35-45 µm |
Tack free | Dry for polishing | Perfect Dry |
25 minutes @ 30˚C | 2 hours @ 30˚C | 2 Days @ 30˚C |
Notes: |
||
The above info is based on laboratory condition and it may vary depending on different climate and environmental condition. * Without thinner (ready to use) or if you want to add, use max 40 ml Medium Reducer |
TDS HARTCRYL 2.1
Fast drying quality two component polyurethane autocryl.Developed for total body repair or panel repair. Good hardness, good weather resistance with good film appearance. |
||
Betta Clear (part A) : – Hardener (part B) : – | ||
Packing size : Part A : – ml Part B : – ml | ||
Mixing ratio * | Viscosity | Pot Life |
2 : 1 (by volume) |
15.9 sec DIN 4 (Part A + Part B) | 2-3 hours |
Hardness pendulum day 7 on pot | Spray Viscosity | Spray Nozzle |
99 (osc,konig) | 14.8 sec NK2 @ 25˚C | 1.3-1.4 |
Spray pressure | Number of Coat | Total film build |
2.0 – 3.0 BAR | 2 Coats | 45-55 µm |
Tack free | Dry for polishing | Perfect Dry |
50 minutes @ 30˚C | 6 hours @ 30˚C | 4 Days @ 30˚C |
Notes: |
||
The above info is based on laboratory condition and it may vary depending on different climate and environmental condition. * Use max 150 ml Medium Reducer |